dc.identifier.citation | Prokopchuk, N. R. Evaluation of internal stress influence on durability of powder paint coatings / N. R. Prokopchuk, T. H. Kukhta // Proceedings of BSTU. No. 4. – Minsk : BSTU, 2014. – P. 49-53 | en |
dc.identifier.uri | https://elib.belstu.by/handle/123456789/14677 | - |
dc.description.abstract | Method for determination of internal stresses influence on durability of powder paint coatings is developed. The method is based on the difference ofthermal-oxidative degradation activation energy of cross ЕD-linked film-forming material within loose and metal-bedded film. It is shown that powder paint coatings internal stresses are insignificant as metal-bedded cross-linked film-forming material does not take big deformations of coatings in the process of their formation as well as during the usage. Reduction of thermal-oxidative degradation activation energy of the parameter ЕDwith such internal stresses is only 3–7 kJ/mol and it does not reduce the coatings durability much in comparison with the influence of the factor of the climatic chamber of UV radiation and high temperatures. | en |
dc.format.mimetype | application/pdf | en |
dc.language.iso | en | en |
dc.publisher | BSTU | en |
dc.subject | порошковые краски | ru |
dc.subject | долговечность покрытий | ru |
dc.subject | лакокрасочные покрытия | ru |
dc.subject | внутренние напряжения | ru |
dc.title | Evaluation of internal stress influence on durability of powder paint coatings | en |
dc.type | Article | en |
dc.identifier.udc | 678.4.023 | - |