Please use this identifier to cite or link to this item:
https://elib.belstu.by/handle/123456789/62621
Full metadata record
DC Field | Value | Language |
---|---|---|
dc.contributor.author | Naizabekov, A. | - |
dc.contributor.author | Lezhnev, S. | - |
dc.contributor.author | Volokitina, I. | - |
dc.contributor.author | Panin, E. | - |
dc.contributor.author | Tolkushkin, A. | - |
dc.contributor.author | Belsky, S. | - |
dc.contributor.author | Pishchov, M. | - |
dc.date.accessioned | 2024-02-03T09:21:30Z | - |
dc.date.available | 2024-02-03T09:21:30Z | - |
dc.date.issued | 2024 | - |
dc.identifier.citation | Investigation of the effect of combined thermomechanical processing on the brass microstructure evolution and the microhardness change / A. Naizabekov [et al.] // Metalurgija. - 2024. - № 2. - P. 283-286. - Bibliogr.: 14 nam. - il. | ru |
dc.identifier.uri | https://elib.belstu.by/handle/123456789/62621 | - |
dc.description.abstract | The article investigates the effect of combined thermomechanical processing, including pre-heat treatment and radial-shear rolling on the brass microstructure evolution and the microhardness change. The microstructure analysis of heat-treated samples according to various modes showed that the most optimal heat treatment before radialshear rolling for L63 brass is annealing at a temperature of 500 °C. As a result of combined thermomechanical processing, a gradient structure was obtained, so in the resulting rods with a diameter of 16 mm in the surface layer, a structure with an average grain size of 9 μm was obtained. In rods with a diameter of 12 mm, a fine–grained, equalgrained structure of 3 μm was obtained in the surface layer. | ru |
dc.format.mimetype | application/pdf | ru |
dc.language.iso | en | ru |
dc.subject | brass | ru |
dc.subject | radial-shear rolling | ru |
dc.subject | heat treatment | ru |
dc.subject | microstructure | ru |
dc.subject | microhardness | ru |
dc.subject | латунь | ru |
dc.subject | прокатка с радиальным сдвигом | ru |
dc.subject | термообработка | ru |
dc.subject | микроструктура | ru |
dc.subject | микротвердость | ru |
dc.title | Investigation of the effect of combined thermomechanical processing on the brass microstructure evolution and the microhardness change | ru |
dc.type | Article | ru |
dc.identifier.udc | 669.35.055:669.5:621.78:620.18 | - |
Appears in Collections: | Публикации в зарубежных изданиях |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Naizabekov A. Investigation of the effect.pdf | 362.4 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.