Formation of luminescent coatings with the tse of low melting glasse

Abstract

The aim of the present research is to develop compounds and technologies for applying the luminous vitrocrystalline compounds to smooth and ribbed glass substrates in LED lamp structure with a remote photoconverter that contains oxide low melting glass as the base and nanostructuredcerium-doped yttrium-aluminum garnet powder as the luminophore. The luminescent coatings basedon nanostructured cerium doped yttrium-aluminum garnet powder and low melting glass of composition Ba()-Bi,0 rB/J rKH)-SiO2 where prepared. YAG.Ce31 powder was synthesized by the method of thermochemical reaction. Silica glass powder was introduced into the composition as diffuse scattering component, improving the lighting characteristics. Spectral-luminescent characteristics of coatings were studied.

Целью настоящего исследования является разработка составов и процесса нанесения люминофорной стеклокристаллической композиции на стеклянные подложки в конструкции светодиодного светильника с удаленным фотопреобразователем, содержащей в качестве основы оксидное легкоплавкое стекло, а в качестве люминофора - наноструктурированный порошок иттрий-алюминиевого граната, активированный ионами церия. Изготовлены люминесцентные покрытия на основе нанострук- турированного порошка иттрий-алюминиевого граната, допированного ионами церия и легкоплавкого стекла на основе ситсте- мы Ba0-Bi:03-B,0rKfD-SiO2. Порошок YAG.Ce* синтезирован методом термохимической реакции. Для улучшения световых и спектрально-люминесцентных характеристик покрытий в состав вводили диффузно-рассеиваюищй компонент - порошок кварцевого стекла. Изучены спектрально-люминесцентные характеристики покрытий.