Studying effects of cerium oxide on optical properties of сolorless glass

Abstract

In glass production, cerium oxide (IV), which is a strong oxidizing agent that converts Fe2+ into Fe3+, is successfully used as a decolorizer. The intensity of light absorption by Fe2+ ions is about 15 times higher than that of Fe3+. At 1200–1400 оС, cerium oxide decomposes 2СеО2 ↔ Се2О3 +1/2О2, i.e. increases the oxidizing potential of the glass mass. The equilibrium is influenced by factors such as temperature, melting time and furnace atmosphere. Cerium oxide simultaneously with decolorization contributes to clarification of the glass mass. The work aimed to study the effect of cerium oxide on optical properties of colorless container glass and to determine the optimal amount of a decolorizing agent.

В стекольном производстве оксид церия (IV), являющийся сильным окислителем, переводящим Fe2+ в Fe3+, успешно применяется в качестве обесцвечивающего агента. Интенсивность поглощения света ионами Fe2+ примерно в 15 раз выше, чем у Fe3+. При 1200–1400 оС оксид церия разлагается по схеме 2СеО2 ↔ Се2О3 +1/2О2, т. е. увеличивает окислительный потенциал стекломассы. На равновесие влияют такие факторы, как температура, время варки и атмосфера печи. Оксид церия одновременно с обесцвечиванием способствует осветлению стекломассы. Целью работы было изучение влияния оксида церия на оптические свойства бесцветного тарного стекла и определение оптимального количества обесцвечивающего агента.