Antibacterial semi-fritted glazes containing iron (III) and manganese (IV) oxides

Abstract

The aim of this research work is production of colored antibacterial glaze coatings for ceramic products containing iron (III) and manganese (IV) oxides. The coatings are produced on the basis of multicalcium aluminoborosilicate frit, dolomite and iron or manganese oxides. The constant components in the raw mixture were feldspar, alumina, coal clay and kaolin. The coatings were obtained by finely grinding the components then applied to the dried semi-finished product and single fired at a temperature of 1200±5 °C for 60±2 minutes. The formation of the glaze layer, the decorative properties of coatings, and their physical and chemical and operational properties were examined. The structural features and phase composition of coatings have been studied. Antibacterial activity of coatings against Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 6538 test strains was determined

Целью работы является получение цветных антибактериальных глазурных покрытий для керамических изделий, содержащих оксиды железа (III) и марганца (IV). Получение покрытий осуществлено на основе многокальциевой алюмоборосили-катной фритты, доломита и оксидов железа или марганца. В качестве постоянных составляющих в сырьевой смеси присутствовали полевой шпат, глинозем, глина огнеупорная и каолин. Покрытия получены тонким помолом составляющих с последующим нанесением на высушенный полуфабрикат и однократным обжигом при температуре 1200+5 °С при продолжительности 60+2 мин. Исследованы процессы формирования глазурного слоя, декоративные свойства покрытий, их физико-химические и эксплуатационные свойства. Изучены особенности структуры и фазового состава покрытий. Определена антибактериальная активность покрытий в отношении тест-штаммов Escherichia coli ATCC 8739 и Staphylococcus aureus ATCC 6538