The Role of Graphite-like Materials in Modifying the Technological Properties of Rubber Composites

Abstract

In this work, general purpose rubber composites were created based on a mixture of nonpolar cis-1,4-isoprene rubber and cis-1,4-divinyl rubber as components. The main filler used was carbon black, while various graphite-like materials (graphite oxide, reduced graphite oxide, expanded graphite, and graphite nanoplatelets) served as additives. It was determined that the addition of these graphite-like materials resulted in a reduction in Mooney viscosity, with the introduction of graphene nanoplatelets having the most significant effect, contributing to a viscosity decrease of 8.5%.

В данной работе были созданы резиновые композиты общего назначения на основе смеси неполярного цис-1,4-изопренового каучука и цис-1,4-дивинилкаучука в качестве компонентов. В качестве основного наполнителя использовалась сажа, а в качестве добавок - различные графитоподобные материалы (оксид графита, восстановленный оксид графита, вспученный графит и графитовые нанопластинки). Было установлено, что добавление этих графитоподобных материалов приводит к снижению вязкости по Муни, причем наиболее значительный эффект оказывает введение графеновых нанопластинок, способствующих снижению вязкости на 8,5%.